Properties of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres Open?Access
文章信息
作者：Wang Shenxiang, Cui Lishan, Wang Guoqing, Zheng Yanjun, Wang Hongxia and Jia Jingsheng
作者單位：
College of Science, China University of Petroleum, Beijing 102249, China and Beijing Research Institute of Chemical Industry, Beijing 100013, China,College of Science, China University of Petroleum, Beijing 102249, China,Beijing Research Institute of Chemical Industry, Beijing 100013, China,College of Science, China University of Petroleum, Beijing 102249, China,Beijing Research Institute of Chemical Industry, Beijing 100013, China and Beijing Research Institute of Chemical Industry, Beijing 100013, China
投稿時(shí)間：2013-03-21
引用方式：Wang, S., Cui, L., Wang, G. et al. Pet. Sci. (2014) 11: 147. https://doi.org/10.1007/s12182-014-0326-5
文章摘要
The oxidation kinetics, surface morphology and phase structure of oxide films grown on 25Cr20Ni alloy in air-H2O and H2-H2O atmospheres at 900 ℃ for 20 h were investigated. The anti-coking performance and resistance to carburization of the two oxide films were compared using 25Cr20Ni alloy tubes with an inner diameter of 10 mm and a length of 850 mm in a bench scale naphtha steam pyrolysis unit. The oxidation kinetics followed a parabolic law in an air-H2O atmosphere and a logarithm law in a H2-H2O atmosphere in the steady-state stage. The oxide film grown in the air-H2O atmosphere had cracks where the elements Fe and Ni were enriched and the un-cracked area was covered with octahedral-shaped MnCr2O4 spinels and Cr1.3Fe0.7O3 oxide clusters, while the oxide film grown in the H2-H2O atmosphere was intact and completely covered with dense standing blade MnCr2O4 spinels. In the pyrolysis tests, the anti-coking performance and resistance to carburization of the oxide film grown in the H2-H2O atmosphere were far better than that in the air-H2O atmosphere. The mass of coke formed in the oxide film grown in the H2-H2O atmosphere was less than 10% of that in the air-H2O atmosphere. The Cr1.3Fe0.7O3 oxide clusters converted into Cr23C6 carbides and the cracks were filled with carbon in the oxide film grown in the air-H2O atmosphere after repeated coking and decoking tests, while the dense standing blade MnCr2O4 spinels remained unchanged in the oxide film grown in the H2-H2O atmosphere. The ethylene, propylene and butadiene yields in the pyrolysis tests were almost the same for the two oxide films.
關(guān)鍵詞
-
25Cr20Ni alloy, air-H2O, H2-H2O, oxide film, anti-coking, resistance to carburization